Adhesive

ABSTRACT

An adhesive containing a far infrared radiation ceramic powder emitting far infrared rays and a radiation source ceramic powder emitting radiations and anions. The radiation source ceramic powder comprises silicon dioxide, aluminum oxide, iron oxide, titanium oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide and zirconium and/or radium. The adhesive according to the present invention relaxes human beings, helps spontaneous recovery from diseases and improves health by the synergistic effects of far infrared rays, anions and radiations.

RELATED U.S. APPLICATIONS

[0001] Not applicable.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

[0002] Not applicable.

REFERENCE TO MICROFICHE APPENDIX

[0003] Not applicable.

FIELD OF THE INVENTION

[0004] The present invention relates to an adhesive.

[0005] The adhesive of the present invention is used, for example, for adhesion between wooden members, between paper members, between leather members, between metallic members, between rubber members, between plastic members, or between ceramic members, or for adhesion between one of these members and another of these members of different materials.

[0006] The adhesive of the present invention is used also for sticking plywood members, laminate lumber members, wall covering, flooring, artificial lawn, ceramic members, etc. to ground materials.

BACKGROUND OF THE INVENTION

[0007] The inventors of the present invention already provided adhesives disclosed by Japanese Patent Laid-Open Publications No. 2000-219858 and No. 2001-200233. These adhesives comprise a basic adhesive such as a vinyl acetate resin emulsion-type adhesive, said basic adhesive being mixed with a far infrared radiation ceramic powder emitting far infrared rays, an absorption/decomposition ceramic powder, an antibacterial ceramic powder, hollow ceramic balls, etc.

[0008] Said far infrared radiation ceramic powder contained in the adhesives of the prior art emits far infrared rays which relax human beings.

[0009] Said absorption/decomposition ceramic powder contained in the adhesives of the prior art absorbs or decomposes harmful chemical substances in the adhesives so as to eliminate bad influences on human beings and bad or irritating smells.

[0010] Said antibacterial ceramic powder contained in the adhesives of the prior art makes an antibacterial action against molds, bacillus coll, staphylococcus aureus, bacillus pyocyaneus, candida bacillus, streptococcus mutans, etc.

[0011] Said hollow ceramic balls are contained in adhesives for wallpaper. The hollow ceramic balls are dispersed in the adhesives so as to adjust the temperature and humidity in the building.

BRIEF SUMMARY OF THE INVENTION

[0012] It is an object of the invention to provide an adhesive which has an anion effect and a radiation hormesis effect synergistically in addition to said relaxation effect by said far infrared radiation ceramic powder contained in the adhesives of the prior art.

[0013] It is another object of the invention to provide an adhesive which helps spontaneous recovery from diseases and improves health.

[0014] These and other objects have been attained by an adhesive containing a far infrared radiation ceramic powder emitting far infrared rays and a radiation source ceramic powder emitting radiations and anions.

[0015] Said radiation source ceramic powder comprises silicon dioxide, aluminum oxide, iron oxide, titanium oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide and zirconium.

[0016] Alternatively, said radiation source ceramic powder may comprise silicon dioxide, aluminum oxide, iron oxide, titanium oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide and radium.

[0017] Or, said radiation source ceramic powder may comprise silicon dioxide, aluminum oxide, iron oxide, titanium oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide, zirconium and radium.

[0018] The adhesives of the present invention include an adhesive containing at least one of said absorption/decomposition ceramic powder, antibacterial ceramic powder and hollow ceramic balls. Also, the adhesives of the present invention include an adhesive containing none of said absorption/decomposition ceramic powder, antibacterial ceramic powder and hollow ceramic balls.

[0019] The iron oxide in the claims and specification includes iron sesquioxide (Fe₂O₃).

[0020] Said far infrared radiation ceramic powder contained in the adhesive relaxes human beings by emitting far infrared rays having a wavelength of 9 to 10 μm. Also, said infrared radiation ceramic powder contained in the adhesive help animals and plants to grow by emitting far infrared rays having a wavelength of 4 to 14 μm.

[0021] Said radiation source ceramic powder contained in the adhesive purifies the blood, balances the autonomic nerve and relieves fatigue by emitting anions. The radiation source ceramic powder emits anions when the ceramic powder is at a standstill or is vibrated or abraded. The radiation source ceramic powder may be natural ores reduced to powder or artificially formed.

[0022] Said radiation source ceramic powder contained in the adhesive emits radiations in small doses. Radiations in small doses have a hormesis effect (radiation hormesis). Radiations in small doses are said to exert a favorable influence on the human body and help spontaneous recovery from diseases. Hormesis is a phenomenon that harmful substances in harmless quantity cause stimulative reactions in living things.

[0023] The adhesive according to the present invention relaxes human beings, helps spontaneous recovery from diseases and improves health by the synergistic effects of said far infrared rays, anions and radiations.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

[0024]FIG. 1 is a graphical representation showing the quantities of anions emitted by a radiation source ceramic powder.

DETAILED DESCRIPTION OF THE INVENTION

[0025] The present invention will now be described in detail.

[0026] The adhesive of the present invention contains a far infrared radiation ceramic powder emitting far infrared rays and a radiation source ceramic powder emitting radiations and anions.

[0027] Said adhesive may contain at least one of an absorption/decomposition ceramic powder, an antibacterial ceramic powder and hollow ceramic balls, in addition to said far infrared radiation ceramic powder and said radiation source ceramic powder.

[0028] A basic adhesive, to which said ceramic powders, etc. are added, may be, for example, a vinyl acetate resin emulsion-type adhesive or a vinyl copolymer resin emulsion-type adhesive.

[0029] Said radiation source ceramic powder comprises, for example, silicon dioxide (SiO₂), aluminum oxide (A₂O₃), iron sesquioxide (Fe₂O₃), titanium oxide (TiO₂), calcium oxide (CaO), magnesium oxide (MgO), potassium oxide (K₂O), sodium oxide (Na₂O) and zirconium (Zr), the percentages by weight thereof being as follows, for example. silicon dioxide: 66.04% aluminum oxide: 19.05% iron sesquioxide:  0.29% titanium oxide:  0.03% calcium oxide:  0.52% magnesium oxide:  0.10% potassium oxide:  6.41% sodium oxide:  6.46% zirconium  0.65%

[0030] The quantities of anions emitted by the radiation source ceramic powder mentioned above were determined as follows.

[0031] About 100 cubic centimeters of the radiation source ceramic powder was scattered about 1 centimeter thick on a table. An ion counter was fixed at a height of about 5 centimeters above the table surface. The quantities of anions emitted by the radiation source ceramic powder were determined for 90 seconds by means of the ion counter. The quantities of anions were determined 10 times in this way. The average quantities of anions determined are shown in FIG. 1.

[0032] The amount of zirconium is about 0.1 to 20% by weight of the total amount of the radiation source ceramic powder.

[0033] Altermitively, said radiall(li S(Ul′CCI ceramic powder inav comprise silicon dioxide, aluminum oxide, iron oxide, titanium oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide and radium.

[0034] In this case the amount of radium is about 0.1 to 20% by weight of the total amount of the radiation source ceramic powder.

[0035] Or, said radiation source ceramic powder may comprise silicon dioxide, aluminum oxide, iron oxide, titanium oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide, zirconium and radium.

[0036] In this case the total amount of zirconium and radium is about 0.1 to 20% by weight of the total amount of the radiation source ceramic powder.

[0037] The radiation source ceramic powder preferably has a radioactive decay of less than 370 Bq per gram.

[0038] Said far infrared radiation ceramic powder emitting far infrared rays has a diameter of about 1 to 44 μm.

[0039] Said radiation source ceramic powder has a diameter of about 1 to 44 μm.

[0040] Said absorption/decomposition ceramic powder has a diameter of about 1 to 44 μm.

[0041] Said antibacterial ceramic powder has a diameter of about 1 to 44 μm.

[0042] Said hollow ceramic balls have a diameter of about 100 μm.

[0043] The adhesive of the present invention is produced as follows. The far infrared radiation ceramic powder and radiation source ceramic powder are put into a container, if necessary along with other ceramic powders mentioned above. Then, a powdered basic adhesive is added to the ceramic powders in the container and these are agitated together.

[0044] Some example of the present invention will now be described.

EXAMPLE 1

[0045] An adhesive was prepared as follows. 2 parts by weight of a far infrared radiation ceramic powder having a diameter of about 3 to 10 μm, 3 parts by weight of a radiation source ceramic powder having a diameter of about 3 to 10 μm, said radiation source ceramic powder containing 3% by weight thereof of zirconium, 3 parts by weight of an absorption/decomposition ceramic powder having a diameter of about 5 to 15 μm, and 1 part by weight of an antibacterial ceramic powder having a diameter of about 3 to 10 μm were put into a container. Then, about 300 parts by weight of a powdered basic material of a vinyl acetate resin emulsion-type adhesive was added to the above in the container and these were agitated together.

EXAMPLE 2

[0046] An adhesive was prepared as follows. 2 parts by weight of a far infrared radiation ceramic powder having a diameter of about 3 to 10 μm, 3 parts by weight of a radiation source ceramic powder having a diameter of about 3 to 10 μm, said radiation source ceramic powder containing 3% by weight thereof of radium, 3 parts by weight of an absorption/decomposition ceramic powder having a diameter of about 5 to 15 μm, and 1 part by weight of an antibacterial ceramic powder having a diameter of about 3 to 10 μm were put into a container. Then, about 300 parts by weight of a powdered basic material of a vinyl acetate resin emulsion-type adhesive was added to the above in the container and these were agitated together.

EXAMPLE 3

[0047] An adhesive was prepared as follows. 2 parts by weight of a far infrared radiation ceramic powder having a diameter of about 3 to 10 μm, 3 parts by weight of a radiation source ceramic powder having a diameter of about 3 to 10 μm, said radiation source ceramic powder containing a total of 3% by weight thereof of zirconium and radium, 3 parts by weight of an absorption/decomposition ceramic powder having a diameter of about 5 to 15 μm, and 1 part by weight of an antibacterial ceramic powder having a diameter of about 3 to 10 μm were put into a container. Then, about 300 parts by weight of a powdered basic material of a vinyl acetate resin emulsion-type adhesive was added to the above in the container and these were agitated together.

[0048] The present invention has the following advantages.

[0049] By the synergistic effects of said far infrared rays, anions and radiations, the adhesive according to the present invention relaxes human beings, helps spontaneous recovery from diseases and improves health. The synergistic effects of said far infrared rays, anions and radiations are not obtained by the adhesives of the prior art mentioned above.

[0050] As many apparently widely different examples of the present invention may be made without departing from the spirit and scope thereof, it is to be understood that the invention is not limited to the specific examples thereof except as defined in the appended claims. 

We claim:
 1. An adhesive containing a far infrared radiation ceramic powder emitting far infrared rays and a radiation source ceramic powder emitting radiations and anions.
 2. An adhesive as claimed in claim 1 wherein said radiation source ceramic powder comprises silicon dioxide, aluminum oxide, iron oxide, titanium oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide and zirconium.
 3. An adhesive as claimed in claim 1 wherein said radiation source ceramic powder comprises silicon dioxide, aluminum oxide, iron oxide, titanium oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide and radium.
 4. An adhesive as claimed in claim 1 wherein said radiation source ceramic powder comprises silicon dioxide, aluminum oxide, iron oxide, titanium oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide, zirconium and radium. 